Wilwood Ultralite UUC BBK Rotors - Cracking

Collapse
X
 
  • Filter
  • Time
  • Show
Clear All
new posts

    #16
    I found HT10's to be very hard on rotors. Not sure if this would promote cracking,
    but they sure seemed to like a lot of heat.

    DTC60 now, and I just don't think about them anymore.

    fwiw,
    t
    now, sometimes I just mess with people. It's more entertaining that way. george graves

    Comment


      #17
      agreed -- I switched from HT-10's to DTC70 and my rotors are lasting forever. DTC60 is my next set just to see if I can tell the difference. DTC70s work way better than the HT-10's for me

      Originally posted by TobyB View Post
      I found HT10's to be very hard on rotors. Not sure if this would promote cracking,
      but they sure seemed to like a lot of heat.

      DTC60 now, and I just don't think about them anymore.

      fwiw,
      t

      Comment


        #18
        I may try another pad. I appreciate the feedback. The HT10s are definitely hard on rotors.

        However, my Massive kit originally came with Coleman rotors of some sort that are NLA. I had about track 8 days with HP+ pads, and another 10 with HT10 pads on that set of rotors!


        Sent from my iPhone using Tapatalk
        -Brandon
        '86 325es S50
        '12 VW GTI Autobahn DSG
        '03 540i M-Sport (sold)